Semiconductor structure with an epitaxial layer and method of manufacturing the same

ABSTRACT

The present invention discloses a semiconductor structure with an epitaxial layer and method of manufacturing the same. The semiconductor structure with the epitaxial layer includes a substrate, a blocking layer on the substrate, multiple recesses formed in the substrate, wherein the recess extends along &lt;111&gt; crystal faces of the substrate, and an epitaxial layer on the blocking layer, wherein the epitaxial layer is provided with a buried portion in each recess and a surface portion formed on the blocking layer.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates generally to a semiconductor structure with an epitaxial layer, and more specifically, to a semiconductor structure with an epitaxial layer buried in recesses of a substrate.

2. Description of the Prior Art

Gallium nitride (GaN) has excellent electric properties, such as high breakdown electric field, high electron saturation velocity, and low on-resistance, etc, so it is suitable to be used as a material for power devices. However, despite it having material characteristics better than conventional silicon material, the most serious problem of GaN material is that it is very difficult to manufacture large-sized chips. Regarding current GaN-on-Si substrate with lowest cost, it is manufactured by growing epitaxial GaN on a Si substrate. Since the coefficient of thermal expansion of GaN is far larger than the one of Si and the crystal lattices of them are highly mismatched, this unsuitable condition is liable to cause problems such as a crack, delamination, or dislocation defect of the GaN epitaxial layer, or wafer warpage issue during film growth or follow-up processing due to the cause of stress.

At present, there are some approaches adopted in the industry to overcome the aforementioned problems during the manufacture of GaN-on-Si substrate, for example, through the growth of multilayered heterogeneous AlGaN buffer layers beforehand on the silicon surface, or using Si substrate with micro patterns to grow the epitaxial structure. Although these approaches can address the aforementioned problems, the issue of high dislocation density and poor heat dissipation is still waiting to be solved urgently. Therefore, it is still needed to further improve structures and relevant manufacturing processes of current GaN-on-Si substrate in the industry.

SUMMARY OF THE INVENTION

In order to further improve the structure of current GaN-on-Si substrate, the present invention provides a novel semiconductor structure, with the feature of an epitaxial layer formed with a buried portion buried in the substrate to improve problems of heat dissipation and defects in conventional GaN-on-Si substrate.

One purpose of the present invention is to provide a semiconductor structure with an epitaxial layer, including a substrate, a blocking layer on the substrate, multiple recesses formed in the substrate, wherein the recess extends along <111> crystal faces of the substrate, and an epitaxial layer on the blocking layer, wherein the epitaxial layer is provided with a buried portion formed in each recess and a surface portion formed on the blocking layer.

Another purpose of the present invention is to provide a method of manufacturing a semiconductor structure with an epitaxial layer, including the steps of providing a substrate, forming a blocking layer on the substrate, wherein the blocking layer has predetermined recess patterns, performing an etch process using the blocking layer as a mask to etch the substrate to form multiple recesses in the substrate, wherein the recess extends along <111> crystal faces of the substrate, and performing an epitaxy process to form an epitaxial layer in the substrate, wherein the epitaxial layer is provided with a buried portion formed in each recess and a surface portion formed on the blocking layer.

These and other objectives of the present invention will no doubt become obvious to those of ordinary skill in the art after reading the following detailed description of the preferred embodiment that is illustrated in the various figures and drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 to FIG. 3 are schematic cross-sections illustrating the process flow of a method of manufacturing a semiconductor structure with an epitaxial layer in accordance with the preferred embodiment of the present invention;

FIG. 4 is a schematic cross-section of a semiconductor structure with an epitaxial layer in accordance with another embodiment of the present invention;

FIG. 5 is a schematic cross-section of a semiconductor structure with an epitaxial layer in accordance with another embodiment of the present invention; and

FIG. 6 is a schematic cross-section of a semiconductor structure with an epitaxial layer in accordance with still another embodiment of the present invention.

DETAILED DESCRIPTION

In the following detailed description of the invention, reference is made to the accompanying drawings, which form a part hereof, and in which is shown, by way of illustration, specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention. Other embodiments may be utilized and structural, logical and electrical changes may be made without departing from the scope of the present invention. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined only by the appended claims, along with the full scope of equivalents to which such claims are entitled.

In general, terminology may be understood at least in part from usage in context. For example, the term “one or more” as used herein, depending at least in part upon context, may be used to describe any feature, structure, or characteristic in a singular sense or may be used to describe combinations of features, structures or characteristics in a plural sense. Similarly, terms, such as “a,” “an,” or “the,” again, may be understood to convey a singular usage or to convey a plural usage, depending at least in part upon context.

It should be readily understood that the meaning of “on,” “above,” and “over” in the present disclosure should be interpreted in the broadest manner such that “on” not only means “directly on” something but also includes the meaning of “on” something with an intermediate feature or a layer therebetween, and that “above” or “over” not only means the meaning of “above” or “over” something but can also include the meaning it is “above” or “over” something with no intermediate feature or layer therebetween (i.e., directly on something).

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper,” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

As used herein, the term “substrate” refers to a material onto which subsequent material layers are added. The substrate itself can be patterned. Materials added on top of the substrate can be patterned or can remain unpatterned. Furthermore, the substrate can include a wide array of semiconductor materials, such as silicon, germanium, gallium arsenide, indium phosphide, etc. Alternatively, the substrate can be made from an electrically non-conductive material, such as a glass, a plastic, or a sapphire wafer.

FIG. 1 to FIG. 3 sequentially illustrates the process flow of the method of manufacturing a semiconductor structure with an epitaxial layer in accordance with the preferred embodiment of the present invention. Please refer to FIG. 1. A substrate 100, such as a silicon substrate, SiC substrate, or sapphire substrate, is first provided to serve as a base for growing the epitaxial layer. A blocking layer 102 is then formed on the substrate 100. For example, use a chemical vapor deposition (CVD) process to form a silicon oxide layer or a silicon nitride layer. The blocking layer 102 would block the surface of the substrate 100, so that epitaxial structure will not be formed on the blocked portion in the epitaxy process. Thereafter, a patterned photoresist 104 is formed on the blocking layer 102. The photoresist 104 is provided with predetermined micro patterns 104 a that may be formed by using advance maskless lithography technology such as E-beam or nano imprint.

In the embodiment of the present invention, micro pattern 104 a may be symmetric pattern such as circle, square, or rectangle uniformly distributed on the surface of the substrate 100 in a predetermined density, with an opening size about 10 nm to 200 nm. The spacing between patterns 104 a is not quite large, preferably double to triple size of the opening. A dry etch process is then performed to the blocking layer 102 using the photoresist 104 as a mask to transfer the patterns 104 a in the photoresist 104 to the blocking layer 102. The pattern 104 a in the blocking layer 102 would expose underlying substrate 100. The patterned photoresist 104 may be removed after patterning the blocking layer 102.

Next, please refer to FIG. 2. After the patterned blocking layer 102 is formed, an etch process is then performed using the patterned blocking layer 102 as an etch mask to form recesses 106 in the substrate. In the embodiment of the present invention, the etch process includes a slope wet etch process, and more specifically, a wet etch process using potassium hydroxide (KOH) etchant to etch the silicon substrate with <100> crystal faces, thereby forming recesses 106 in diamond shape extending along the <111> crystal faces in the substrate 100, as shown in the figure. In the embodiment of the present invention, these recesses 106 with particular shape may shape the epitaxial structure formed therein to have corresponding shape in order to achieve the efficacy required by the present invention.

Next, please refer to FIG. 3. After the diamond-shaped recesses 106 are formed, an epitaxy process is then performed to form an epitaxial layer 108 on the substrate. The material of epitaxial layer 108 may be gallium nitride (GaN) or aluminum gallium nitride (Al_(x)Ga_(y)N). Since the presence of the blocking layer 102, the epitaxial layer 108 would start to grow only from the surface of substrate 100 not covered by the blocking layer 102, i.e., from the surface of the recesses 106. Although the epitaxial layer 108 in the embodiment of the present invention start to grow from respective recesses 106, they will merge into a common epitaxial structure completely covering the entire surface of the substrate 100 after growing out of the recesses 106. In the embodiment of the present invention, the epitaxial layer 108 includes a buried portion 108 a formed in each recess 106 and a surface portion 108 b formed on the blocking layer 102. In addition, a middle portion 108 c is formed in the blocking layer 102 between the buried portion 108 a and the surface portion 108 b to connect therebetween.

Refer again to FIG. 3. In the embodiment of the present invention, since the epitaxial layer 108 is formed from the surface of the substrate 100, it can be seen from the figure that voids 110 would be formed between the surface portion 108 b of the epitaxial layer and the blocking layer 102, wherein each void 110 is formed respectively between two buried portions 108 a. The formation of voids 110 between the epitaxial layer 108 and the blocking layer 102 may help to release stress on the epitaxial interface and solve the crack problem result from the lattice mismatch between the materials of epitaxial structure and the substrate. In addition, since the buried portion 108 a of the epitaxial layer 108 formed in the recess 106 is in diamond shape, the shear stress generated at the epitaxial interface during thermal cycle may be effectively transformed into compressive stress to avoid wafer warpage or delamination. Furthermore, the buried portions 108 a buried in the substrate may significantly increase the contact area between the epitaxial layer 108 and the substrate to improve the efficiency of heat dissipation of the entire substrate. Lastly, since the epitaxial layer 108 grows from the surface of the recesses 106 with <111> crystal faces, the inherent dislocation defects between the epitaxial layer and the substrate would be confined in the recesses 106 and would not spread upwardly to the surface portion 108 b of the epitaxial layer 108, so that the surface portion 108 b of the epitaxial layer 108 that would be used practically in the process would have excellent epitaxial properties.

After the epitaxial layer 108 is formed on the entire surface of the substrate, semiconductor devices such as light-emitting diode (LED) or power device may be then manufactured on the epitaxial layer 108. Since those semiconductor devices and relevant features are not the key points of the present invention, they will not be further described in the disclosure.

Please refer to FIG. 4, which is a schematic cross-section of a semiconductor structure with an epitaxial layer in accordance with another embodiment of the present invention. As shown in FIG. 4, in this embodiment, void 112 may be formed inside the buried portion 108 a of the epitaxial layer 108 in the recess 106. These voids 112 may also help to release the stress of the epitaxial layer. On the other hand, there may be no voids formed between the epitaxial layer 108 and the blocking layer 102.

Please refer to FIG. 5, which is a schematic cross-section of a semiconductor structure with an epitaxial layer in accordance with another embodiment of the present invention. In the embodiment of the present invention, a buffer layer 114 may be formed on the surface of the recesses 106 before performing the epitaxy process. The buffer layer 114 may have compositions similar to the epitaxial layer 108. For example, when the material of epitaxial layer 108 to be formed is GaN, the material of the buffer layer 114 may be selected from AlN or Al_(x)Ga_(y)N. The buffer layer 114 may further mitigate the problem of lattice mismatch between the epitaxial layer 108 and the substrate 100, so that the epitaxial layer 108 to be formed thereon in later process would have a better quality.

In other embodiment, for example in the condition that the slope wet etch process is not performed completely, the recess 106 formed in the substrate 100 may be in incomplete diamond shape with a horizontal bottom surface, as shown in FIG. 6.

Those skilled in the art will readily observe that numerous modifications and alterations of the device and method may be made while retaining the teachings of the invention. Accordingly, the above disclosure should be construed as limited only by the metes and bounds of the appended claims. 

What is claimed is:
 1. A semiconductor structure with an epitaxial layer, comprising: a substrate; a blocking layer on said substrate; multiple recesses formed in said substrate, wherein said recess is in diamond shape; and an epitaxial layer on said blocking layer, wherein said epitaxial layer is provided with a buried portion formed in each said recess and a surface portion formed on said blocking layer.
 2. The semiconductor structure with an epitaxial layer of claim 1, further comprising multiple voids formed between said surface portion of said epitaxial layer and said blocking layer.
 3. The semiconductor structure with an epitaxial layer of claim 2, wherein each said void is formed respectively between two said recesses.
 4. The semiconductor structure with an epitaxial layer of claim 1, wherein voids are formed within said buried portion of said epitaxial layer.
 5. The semiconductor structure with an epitaxial layer of claim 1, wherein said epitaxial layer further comprises a middle portion in said blocking layer.
 6. The semiconductor structure with an epitaxial layer of claim 1, further comprising a buffer layer formed on a surface of said recess.
 7. The semiconductor structure with an epitaxial layer of claim 1, wherein a material of said buffer layer is aluminum nitride or aluminum gallium nitride (Al_(x)Ga_(y)N).
 8. The semiconductor structure with an epitaxial layer of claim 1, wherein said recess extends along <111> crystal faces of said substrate.
 9. The semiconductor structure with an epitaxial layer of claim 1, wherein said recess has a horizontal bottom surface.
 10. The semiconductor structure with an epitaxial layer of claim 1, wherein said substrate is a silicon substrate with <100> crystal faces.
 11. The semiconductor structure with an epitaxial layer of claim 1, wherein a material of said epitaxial layer is gallium nitride or aluminum gallium nitride (Al_(x)Ga_(y)N).
 12. The semiconductor structure with an epitaxial layer of claim 1, wherein said epitaxial layer is formed on an entire surface of said substrate.
 13. A method of manufacturing a semiconductor structure with an epitaxial layer, comprising: providing a substrate; forming a blocking layer on said substrate, wherein said blocking layer is provided with predetermined recess patterns; performing an etch process using said blocking layer as a mask to etch said substrate to form multiple recesses in said substrate, wherein said recess is in diamond shape; and performing an epitaxy process to form an epitaxial layer in said substrate, wherein said epitaxial layer is provided with a buried portion formed in each said recess and a surface portion formed on said blocking layer.
 14. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, wherein said epitaxy process further comprises forming multiple voids between said surface of said epitaxial layer and said blocking layer.
 15. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 14, wherein each said void is formed respectively between two said recesses.
 16. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, further comprising forming abuffer layer on a surface of said recess before performing said epitaxy process.
 17. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, wherein said etch process comprises slope wet etch process.
 18. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, further comprising: forming a photoresist on said blocking layer; performing an electron beam photolithographic process to form said recess patterns in said photoresist; performing another etch process using said photoresist as a mask to form said recess patterns in said blocking layer; and removing said photoresist.
 19. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, wherein said recess extends along <111> crystal faces of said substrate.
 20. The method of manufacturing a semiconductor structure with an epitaxial layer of claim 13, wherein said substrate is a silicon substrate with <100> crystal faces. 